PC03-MT-100

Brady PCM PC03-MT-100 consists of a thermally conductive, 60 °C phase change compound coated on a thermally conductive polyimide film. The polyimide reinforcement makes the material easy to handle and the 60 °C phase change temperature minimizes potential problems during shipping and handling. PC03-MT-100 achieves superior values in voltage breakdown and thermal performance when compared to its competition. The product is supplied on an easy release liner for exceptional handling during high volume manual assemblies. SEDO suggests the use of spring clips to assure constant pressure with the interface and power source. Please refer to thermal performance data to determine nominal spring pressure for your application.

Features and Benefits

• Thermal impedance: 0.15 °C·in.2/W (@10 psi)
• Field-proven polyimide film
• excellent dielectric performance
• excellent cut-through resistance
• Outstanding thermal performance in an insulated pad

Typical Properties

PHYSICAL	TYPICAL RESULTS	TEST METHOD
Color	Yellow	Visual
Reinforcement Carrier	Polyimide	-
Thickness	0.1mm	ASTM D374
Elongation at break	30%	ASTM D828
Density	1.8 g/cc	ASTM D792
Hardness (Shore A)	90	ASTM D2240
Tensile Strength	14N/mm²	ASTM D828
Volume resistivity	1x10¹²Ω⋅cm	ASTM D257
Dielectric Strength	5000 volts	ASTM D149
Continuous Use Temperature	-40-150°C	-
Phase Change Temperature	60°C	-
Thermal Impedance @ 10psi	0.15°C·in.²/W	ASTM D5470

Typical Applications

• Spring / clip mounted
• Discrete power semiconductors and modules

Available Forms

• Roll form, die-cut parts and sheet form